Nanocrystalline Ribbon 1K107B
Compared with traditional ferrite, nanocrystalline materials have high saturation flux density (≥1.2T), low core losses, low coercivity, low or zero magnetostriction, wide adjustable permeability in the range from 400 to 900,000, and excellent thermal stability, making it an ideal choice for high-frequency power electronics.
- Description
- Online Inquiry
Applications
Nanocrystalline ribbon 1K107B is mainly applied in the production of advanced common mode chokes, high frequency power transformers, precision current transformers, magnetic amplifiers and magnetic shielding sheets, etc.
Product Features
|
Width |
2~50mm | Thickness |
16~26μm |
|
Saturation hysteresis expansion coefficient λs(ppm) |
1 | Curie Temperature(℃) | 570 |
|
Saturate induction Bs(T) |
1.23 |
Crystallization(℃) |
510 |
|
Coercivity Hc(A/m) |
1.5 |
Density(g/cm3) |
7.25 |
| Resistivity( μΩ.m) | 1.2 | Hardness Hv(kg/mm²) |
880 |
Related Products
-
Amorphous Ribbon 1K101
Amorphous Ribbon is an new soft magnetic material. It is produced through the advanced technology of rapid solidification of molten metal at a cooling rate of about a million ℃/sec. During this process the metal is rapidly quenched as a form of ribbon with 25-35 μm thickness, and the micro-structure of the alloy is the amorphous due to the high quenching rate
-
Nanocrystalline Ribbon 1K107
Fe-based Nanocrystalline Ribbon has the properties of high saturation magnetization and permeability, low coercive force and core loss, good stabilities on temperature and time effect, excellent abilities of anti-wearing and anti-rusty, and it shows the best property-value ratio among all of the soft magnetic materials